• Model NO.：As per drawings
• Coating：as Per Requirement
• Machining Tolerance：as Per Drawings
• Standard：GB
• Certification：CE, ISO 9001:2000
• HSS Rolls：Used as Work Rolls in Finishing Stands.
• Our Advantage：Rich Experience, Best Service, Professional Team.
• Our Customers：Russia,Turkey, Bangladesh, Columbia,Vietnam
• Inspection：Ut, Metallographic Examination, Hardness Test etc.
• Plant：We Have Our Own Factory
• Exhibition：We Always Attend Some Exhibition in Abroad.
• Specifications：High Dimension Accuracy, Wear Resistance
• After Sales Service：Engineer Available to Service Machinery Overseas
• Application：Hot Strip Mills,Bar Mills, Universal Section Mills
• OEM：We Can Also Accept The Trail Order.
• Transport Package：Metal Pallet or Wooden Case
• Specification：as per drawing
• Trademark：WEILANG
• Origin：China
• HS Code：84553000
• Production Capacity：28000 Tons, Year

Grade

C

Si

Mn

P

S

Cr

Ni

Mo

V

AD 140

1.30-1.50

0.30-0.60

0.70-1.10

≤0.035

≤0.030

0.80-1.20

0.50-1.20

0.20-0.60

 

AD 160

1.50-1.70

0.30-0.60

0.80-1.30

≤0.035

≤0.030

0.80-2.00

≥0.20

0.20-0.60

 

AD 180

1.70-1.90

0.30-0.80

0.60-1.10

≤0.035

≤0.030

0.80-1.50

0.50-2.00

0.20-0.60

 

AD 190

1.80-2.00

0.30-0.80

0.60-1.20

≤0.035

≤0.030

1.50-3.50

1.00-2.00

0.20-0.60

 

3.Mechanical Properties
 

Tensile Strength (kg/mm²)

550-700

Bending Strength (kg/mm²)

750-1000

Elongation (%)

0.4-2.0

4. Equipments


5.Machining



6.Inspection and Delivery


7. The Operation of Rolls
1.) Clean off grease, dust and rust from roll surface before taking regular inspection, pay special attention to roll surface, there should be no marks, bruises,rust or cracks on roll surface, do not use the roll on mill with surface cracks.
2.) Before rolling starts, check carefully the surface quality, material and hardness of steel strips to be rolled, strips joint areas should be smooth and without bumps.
3.) For high speed, wide range and large reduction rolling practice, or when environment temperature is low, carry out pre-heating practice to the roll before rolling starts. Under normal rolling condition, run the mill in low speed for re-heating before rolling starts.
4.) Carry out re-grinding practice strictly according to roll management regulation, do not wait until surface defects are found before re-grinding. For each time of re-grinding, make sure to remove completely the fatigue layer and re-hardening layer from the rolls.
5.) Make sure to spray cooling water onto the rolls evenly and fully during rolling, so as to avoid hardness drops or cracks generation of rolls due to high working temperature or regional high temperature.
6.) Roll journal should be properly lubricated and cooled, so as to avoid excessive heat which may damage roll journal surface. Bearing should be fully lubricated and cooled as well to avoid journal break down.
7.) Rolling environment and strip surface should beclean, falling of foreign matters or ply rolling are not allowed.
8.) Avoid rolling accidents caused by sticking, chew-up, strip break or skidding, in case these accidents occurs, replace the work rolls, intermediate rolls and back-up rolls immediately, and carry out inspection and re-grinding accordingly.

TANGSHAN WEILANG is a full integrative enterprise who is dedicated to design, production, sales and service in metallurgical products.Our products contain various mill rolls and roll rings for different kinds of bar&wire mills, section mills, plate&strip mills, tube mills etc., which has been supplied to 20 countries and regions including Southest Asia, Europe, North America and Middle East.