• Coating：Sodium silicate
• Machining Tolerance：+,-0.01mm
• Standard：AISI
• Certification：CE, ISO 9001:2000
• Name：Slag Pot
• Slag Pots in Cast Steel：Heavy Fabrication Division
• Materia：DIN 17182 GS-16mn5 1.1131
• Fact Cubage：22 Cbm
• Weight：10 -100 T
• Product Application：Slag Pot in Steel Works.
• Cast Tolerance：Unless Otherwise ASTM, En, DIN, ISO, JIS, GB
• Quality System：ISO 9001
• Pattern：New Natural Wooden Mold;
• Quality Inspection：Chemical Analysis; -Mechanical Performance; -Dim
• Transport Package：Slag Pots in Cast Steel & Slag Ladle
• Specification：Slag Pots in Cast Steel & Slag Ladle
• Trademark：CITICIC
• Origin：Luoyang, Henan
• Production Capacity：2000PCS,Year

Feature:
Material: steel, self-smelting according to standard: ASTM, EN, DIN,ISO, JIS, GB, etc;
Sand mold casting: Steel casting, through sodium silicated-bonded sand and/or resin sand;
Pattern: new natural wooden mold;
Non-destructive examination:
-visual detection ;
-Ultrasonic test ;
-Magnetic particle inspection ;
Quality inspection:
-Chemical analysis;
-Mechanical performance;
-Dimension report;
Cast Tolerance: unless otherwise  ASTM, EN, DIN,ISO, JIS, GB
Machining tolerance: unless otherwise according to dwg. requirement;
 
The expertise of CITICIC  arises from its privilege to be both user and manufacturer of slag 
pots. The extensive experience gained in designing and engineering slag-pots is primarily based on the 
pots operating at the own steel plant and secondly on about 3.000 items produced over the 40 last years 
also in co-operation with manufacturers of slag pot carriers and service providers to metallurgical 
industries. 
The Dillinger slag pots are operating worldwide whereverreliable tools are required for the disposal of 
molten or solid slag which arises from metallurgical or chemical processes. 
Heavy Fabrication Division
Product definition 
The product covered here is a load-bearing device whose sole purpose is to collect molten or solid slag 
generated during metallurgical or chemical processes, to retain it during transport and to deposit it at a 
place of disposal. 
Slag pots are crucial items as they are part of a lifting equipment and therefore undergo in terms of 
mechanical design engineering and handling the national safety regulations of the state where they are 
supposed to be operated. The design of the Dillinger slag pots intended to be used within the European 
Community meets the requirements ofthe European Machinery Directive 2006/42/EC: every slag pots is 
supplied with the CE conformity marking. 
Material 
The pots are made out of the cast-steel DICAST, trade name owned by CITICIC for 
castings: this material is similar to the steels A27/A 27M grade 65-35: April 2003, BS 3100 A1/A2: 
January 1991 or GS 20Mn5 to DIN 17182: May 1992. DICAST is a fully killed steel, vacuum-degassed 
and processed to a fine grain size structure with improved properties both in toughness and in elongation. 
  Chemical compositionverified on product 
Elements C  Si  Mn  P  S 
Required  ≤0.23%  ≤0.55%  ≤1.65%  ≤0.025%  ≤0.025% 
Typical 0.17%  0.40%  1.45% 0.015% 0.002% 
  Mechanical propertieschecked at room temperature in the delivery condition i.e. after completion of 
the quality heat treatment from cylindrical cast-on test blocks (60 mm x 250 mm) available on 
every slag pot: both the sample preparation and the testing comply with ASTM A 370-96. 
Properties Rm Reh
 A  KCV ( average of 3 specimens / individual )  Required  ≥450 MPa  ≥240 MPa  ≥20 %  ≥55 J / 39 J 
Typical  490 MPa  280 MPa  30 %  120 J / 85 J 
  Delivery condition: normalised
Note regarding the material selection: due to obvious advantages in terms of service life and maintenance 
cost-efficiency, cast steel has been becoming more significant in the slag pot construction over the last 
years versus both materials, spheroidal cast-iron and lamellar graphite cast-iron. In contrast to other 
materials, cast steel offers excellent repair possibilities as it is well-suited to welding. 
Manufacturing 
Except the supply of the forgings for trunnions and the engineering of the pattern, all further operations 
are carried-out at the in-house foundry plant. 
  Moulding
the castings are manufactured in a workman-like manner as required in the China standard DIN EN 
1599-1: August 1997, ruling the delivery conditions ofcastings. The moulding is individually carried 
out within a modular flask by using a sand preparation based on resin bonding. 
FAQ

After Sales Service

ZTIC Heavy Industries is your business partner in the After Market.
ZTIC  able to provide:
1.    ENGINEERED SPARES -  DESIGN AND MANUFACTURING
2.    LARGE VOLUME STEEL AND IRON CASTING FOUNDARIES
3.    HUGE MACHINE SHOP CAPABILITIES
4.    TRAINING PROGRAMMES
5.    PREVENTATIVE MAINTENANCE PROGRAMS
6.    PREVETATIVE MAINTENANCE SERVICES
7.    COMPREHENSIVE MAINTENANCE PROGRAMS